Amorphous nanocrystalline alloy strip
1. The name iron-based nanocrystalline alloy strip
Pieces with iron-based nanocrystalline alloy strip material, strip width naming, naming format is as follows:
For example: FN - 010 and FN - 50 respectively width of 10 mm wide and 50 mm of iron-based nanocrystalline alloy strip.
2. The performance characteristics
Mixer iron-based nanocrystalline alloy is a new kind of soft magnetic alloy material, he is a metallic element Fe, Cu, Nb and metalloid elements Si, B, special purpose also contains trace Mo, Ni, Co and other metal elements. Adopt international advanced rapid cooling fast quenching technology, the molten metal at 106 ℃ / s direct cooling, made the thickness of 25 ~ 35 m iron base amorphous alloy thin strip. The alloy thin belt part by annealing crystallization processing, internal can form uniform nanometer crystal particles (10 ~ 20 nm in diameter) and amorphous phase dual phase structure, so called the nanocrystalline alloy or superfine crystal alloy, it is because of this kind of dual phase structure makes it have excellent soft magnetic properties.
Mixer iron-based nanocrystalline alloy strip has high saturation magnetic induction intensity, the high initial and maximum magnetic permeability, low coercive force, low loss, approaching zero saturation magnetostriction coefficient and good temperature stability, and permalloy and Co based amorphous alloy, but with a higher saturated magnetic induction intensity of Bs (1.3 T), has a large number of alternative silicon steel, permalloy and ferrite, widely used in the current systems and electronic fields.
3. The application field
Pieces of EMC filter common-mode inductor core
Pieces of high frequency switching power supply transformer magnetic core
Pieces of high frequency inverter transformer magnetic core
Pieces of precision current transformer core
Pieces of power system measuring current transformer core
In pieces zero sequence current transformer core
Magnetic core pieces of magnetic amplifier
4. Basic performance iron-based nanocrystalline alloy
The physical properties of typical pieces iron-based nanocrystalline alloy
Saturated magnetic induction intensity of Bs (T) 1.25 vickers hardness Hv (kg/was) 880
Curie temperature Tc (℃ 560 ℃) density (g/cm3) 7.25 d
Tx crystallization temperature (510 ℃) ℃ resistivity rho (including Ω · cm) 130
Saturation magnetostriction coefficient of lambda s 2 x 10-6 continuous working temperature (℃) - 55 ~ 130
5. The iron-based nanocrystalline alloy strip specifications
6. Typical magnetization curve iron-based nanocrystalline alloy strip
7. 铁基纳米晶合金带材典型损耗角关系